1001 Chlorinated Rubber Based Road Marking Paint OCR2SG is formulated specifically with high quality non reactive corrosion- inhibitive pigments and extenders properly blended with non permeable plasticisers, synthetic binders and high aromatic content solvents to encounter severe tropical, climatic and adverse atmospheric conditions prevailing in country. These composite systems have excellent water and ultraviolet rays resistant, mild acid and alkali, and fungus resistance.

1.  Form Free flowing liquid without hard settling

2. Drying Time

A) Surface Drynot more than 30 minutes

B) Hard Dry not more than 2 Hours

C) Tack Free12  to 18 Hours

3.  Consistency with Ford Cup B460 to 65 seconds at 30°C

4.  ColourWhite, Golden Yellow, Black, Any shade on request

5.  Finishing Smooth & Eggshell to Matt

6.  Specific Gravity at 27°CMinimum 1.1

7. Wet Opacity  8 to 10 sq metre per litre (As Per IS 101)

8. Drying Film Thickness   Minimum 25 Microns

9.  Fastness to LightPasses as IS 101

10.  Scratch Hardness Passes the load of 1.0 kg (As per IS 101)

11. Flexibility and Adhesion No detachment of film, and passes ½ Mandrel test

       after 96 hours of air drying

12. Stripping TestFree flow Jagged edges

13. Resistance to Water90% Gloss Retention of Immersed Portion (No effect)

14. Flash Point Not below 25°C

15. Salt Spray TestNo corrosion or spot formation was visible even after 96 hours of

continuous salt spray

16. Keeping Properties Not more than six months from the date of manufacturing.

17. Use This paint is recommended for newly plastered and concrete roads

where normal road marking paint as per IS specification fails.

This coating is fast drying in nature and non stripping with matt to

eggshell finish so it is most suited on a concrete road.